Paramèt pwodwi grafit elektwòd

Kouran kapasite pote

Nomina dyamèt		R		H		Uhp
Nomina dyamèt		Kouran kapasite pote	Dansite aktyèl	Kouran kapasite pote	Dansite aktyèl	Kouran kapasite pote	Dansite aktyèl
nan	mm	A	A/cm2	A	A/cm2	A	A/cm2
12	300	10000-13000	14-18	13000-17400	17-24	15000-22000	20-30
14	350	13500-18000	14-18	17400-24000	17-24	20000-30000	20-30
16	400	18000-23500	14-18	21000-31000	16-24	25000-40000	19-30
18	450	22000-27000	13-17	25000-40000	15-24	32000-45000	19-27
20	500	25000-32000	13-16	30000-48000	15-24	38000-55000	18-27
22	550	32000-40000	13-16	35000-55000	14-22	42000-64000	17-26
24	600	35000-41000	13-15	41000-61000	14-21	50000-73000	17-25
28	700	39000-48000	10-12	55000-82000	14-21	67000-99000	17-25
32	800	43000-54000	8-10	/	/	/	/

Byenveni nan kontakte nou pou sitasyon pi ba.

Imèl: info@zaferroalloy.com

Adrès: Huafu Commercial Center, Wenfeng Distri, Anyang City, Henan Pwovens, Lachin

Wòl Graphite a kòm yon materyèl electrodes nan founo elektrik ark (EAFS) se unik, kondwi pa pwopriyete inik li yo fizik ak chimik ki adrese demand yo ekstrèm nan ark - ki baze sou steelmaking.

Poukisa Graphite?

Segondè pwen k ap fonn: Grafit sublimes nan ~ 3,600 degre, byen lwen depase EAF tanperati opere (1,500-3,000 degre), asire entegrite estriktirèl.

Ba rezistivite: Avèk rezistivite osi ba ke 15 μω · m, grafit minimize pèt enèji pandan transmisyon aktyèl, diminye depans operasyonèl yo.

Rezistans chòk tèmik: Ekspansyon ki ba Graphite a tèmik (2-4 × 10⁻⁶/ degre) pèmèt li kenbe tèt avè fluctuations tanperati rapid (egzanp, inisyasyon arc/ sispansyon) san yo pa fann.

Rezistans oksidasyon: Nan 1,500-3,000 degre, grafit oksidasyon tou dousman konpare ak metal oswa seramik, pwolonje lavi electrodes.